| Raw Material: | Synthetic Rubber |
|---|---|
| Material: | Butyl Rubber |
| Appearance: | Bale |
| Form: | The Massive Raw Rubber |
| Color: | White to Light Yellow |
| Model: | Br9000 |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
| Product Name | BUTADIENE RUBBER BR9000 | Ref. Code |
GB/T 8659-2018
|
|
| No. |
Inspection Item
|
Index
value
|
Actual data | Inspection Procedure |
| 1 | Appearance | |||
| 2 |
Volatile Matter / %
|
≤0.50 | 0.30 | GB/T 24131.1 |
| 3 |
Ash Content / %
|
≤0.20 | 0.025 | GB/T 4498 |
| 4 |
Mooney Viscosity[ML(1+4) 100ºC]
|
45±4 | 44 | GB/T 1232.1 |
| 5 |
Compound Mooney Viscosity[ML(1+4) 100ºC]
|
≤65 | 54 | GB/T1232.1 |
| 6 | 300%Modulus/MPa | |||
| 145° C, 25min | 7. 0~12.0 | 10. 19 | GB/T 8660 | |
|
145° C, 35min
|
8. 0~13.0
|
11. 03 | GB/T 8660 | |
|
145° C, 50min
|
8. 0~13.0 | 10. 24 | GB/T 8660 | |
| 7 | Tensile Strength | ≥13.2 | 16.79 | GB/T 8660 |
| 8 | Elongation(145ºC, 35min) /% | ≥330 | 406 | GB/T 8660 |
| 9 | Packing thickness,mm | ≤0.3 | 0.060 |
Q/TFHC ZL J32
|
| 10 |
Melting Point of PE Film ,ºC
|
≤110 | 102 | Q/TFHC ZL J32 |
Suppliers with verified business licenses
Audited Supplier 